Cement grains with surface-synthesized carbon nanofibres: Mechanical properties and nanostructure

Petr Hlavacek, Vit Smilauer, Pavel Padevet, Larisa Nasibulina, Albert G. Nasibulin

Tutkimustuotos: Artikkeli kirjassa/konferenssijulkaisussaConference contributionScientificvertaisarvioitu

6 Sitaatiot (Scopus)

Abstrakti

The carbon nanotubes were synthetized directly on the surface of Portland cement particles. Mixing this new carbon/cement material with ordinary cement creates a modified cementitious substance, where carbon is perfectly dispersed in the volume. In presented work, the fracture energy and compressive strength of cement paste/mortar created from this new material was measured. The composites with weight fractions of carbon nanotubes/paste in the ranges 0-0.038 were prepared and mechanically tested. Slight increase in fracture energy and compressive strength was observed even in the low carbon weigh fraction 0.019.

AlkuperäiskieliEnglanti
OtsikkoNANOCON 2011 - Conference Proceedings, 3rd International Conference
Sivut75-80
Sivumäärä6
ISBN (elektroninen)9788087294277
TilaJulkaistu - 2011
OKM-julkaisutyyppiA4 Artikkeli konferenssijulkaisuussa
TapahtumaInternational Conference on Nanomaterials: Research & Applications - Brno, Tshekki
Kesto: 21 syyskuuta 201123 syyskuuta 2011
Konferenssinumero: 3

Conference

ConferenceInternational Conference on Nanomaterials
LyhennettäNANOCON
MaaTshekki
KaupunkiBrno
Ajanjakso21/09/201123/09/2011

Sormenjälki

Sukella tutkimusaiheisiin 'Cement grains with surface-synthesized carbon nanofibres: Mechanical properties and nanostructure'. Ne muodostavat yhdessä ainutlaatuisen sormenjäljen.

Siteeraa tätä