Black Bioinks from Superstructured Carbonized Lignin Particles

Bruno Dufau Mattos*, Noora Jäntti, Sergei Khakalo, Ya Zhu, Arttu Miettinen, Joni Parkkonen, Alexey Khakalo, Orlando Rojas*, Mariko Ago*

*Tämän työn vastaava kirjoittaja

Tutkimustuotos: LehtiartikkeliArticleScientificvertaisarvioitu

3 Sitaatiot (Scopus)
27 Lataukset (Pure)

Abstrakti

A renewable source of carbon black is introduced by the processing of lignin from agro-forestry residues. Lignin side streams are converted into spherical particles by direct aerosolization followed by carbonization. The obtained submicron black carbon is combined with cellulose nanofibers, which act as a binder and rheology modifier, resulting in a new type of colloidal bioink. The bioinks are tested in handwriting and direct ink writing. After consolidation, the black bioinks display total light reflectance (%R) at least three times lower than commercial black inks (reduction from 12 to 4%R). A loading of up to 20% of nanofibers positively affects the cohesion of the dried bioink (1 to 16 MPa), with no significant reduction in light reflectance. This is a result of the superstructuring of the ink components, which disrupts particle packing, intensifies colloidal interactions, introduces light absorption, and non-reflective multiple scattering.
AlkuperäiskieliEnglanti
Artikkeli2304867
Sivumäärä11
JulkaisuAdvanced Functional Materials
Vuosikerta33
Numero45
Varhainen verkossa julkaisun päivämäärä5 heinäk. 2023
DOI - pysyväislinkit
TilaJulkaistu - 2 marrask. 2023
OKM-julkaisutyyppiA1 Alkuperäisartikkeli tieteellisessä aikakauslehdessä

Sormenjälki

Sukella tutkimusaiheisiin 'Black Bioinks from Superstructured Carbonized Lignin Particles'. Ne muodostavat yhdessä ainutlaatuisen sormenjäljen.

Siteeraa tätä