Austempering experiments of production grade silicon solution strengthened ductile iron

Kaisu Soivio*

*Tämän työn vastaava kirjoittaja

Tutkimustuotos: Artikkeli kirjassa/konferenssijulkaisussaConference contributionScientificvertaisarvioitu

Abstrakti

Austempered ductile iron provides a feasible way to produce high strength components. However, in heat treatments resulting in highest strengths some of the ductility is lost due to formation of bainitic carbides. The role of silicon in inhibiting the formation of iron carbides in ascast ductile irons as well as its solution strengthening effect is well known and acknowledged in industry. The effect of silicon on austemperability, resulting microstructures, and mechanical properties of austempered ductile irons with silicon contents with 3.4-3.8 w-% was researched. Quenching and austempering heat treatments were carried out for production grade silicon solution strengthened ductile irons EN GJS 500-14. Results indicate, that it is possible to manufacture a fully ausferritic structure into a silicon solution strengthened matrix and indeed good ductility can be achieved in combination with ultimate tensile strength of 1600 MPa. Segregation of silicon reduces the solubility of carbon into the matrix especially close to the graphite nodules which reduce the stability of carbon stabilized austenite and leads into compromised machinability.

AlkuperäiskieliEnglanti
OtsikkoScience and Processing of Cast Iron XI
KustantajaTRANS TECH PUBLICATIONS
Sivut239-245
Sivumäärä7
ISBN (painettu)9783035710557
DOI - pysyväislinkit
TilaJulkaistu - 1 tammikuuta 2018
OKM-julkaisutyyppiA4 Artikkeli konferenssijulkaisuussa
TapahtumaInternational Symposium on the Science and Processing of Cast Iron - Jonkoping, Ruotsi
Kesto: 4 syyskuuta 20177 syyskuuta 2017
Konferenssinumero: 11

Julkaisusarja

NimiMaterials Science Forum
Vuosikerta925 MSF
ISSN (painettu)0255-5476

Conference

ConferenceInternational Symposium on the Science and Processing of Cast Iron
LyhennettäSPCI-XI
Maa/AlueRuotsi
KaupunkiJonkoping
Ajanjakso04/09/201707/09/2017

Sormenjälki

Sukella tutkimusaiheisiin 'Austempering experiments of production grade silicon solution strengthened ductile iron'. Ne muodostavat yhdessä ainutlaatuisen sormenjäljen.

Siteeraa tätä