An origin of good electrical conduction in La4BaCu5O13+δ

De. Mori, S. Asai, I. Terasaki, R. Okazaki, Y. Yasui, Outi Parkkima, Maarit Karppinen

    Tutkimustuotos: LehtiartikkeliArticleScientificvertaisarvioitu

    3 Sitaatiot (Scopus)
    270 Lataukset (Pure)

    Abstrakti

    We have prepared a set of polycrystalline samples of the metallic copper oxide La4BaCu5−xCoxO13+δ (0 ≤ x ≤ 0.35) and have measured the resistivity from 4 to 800 K. All the resistivities show metallic temperature dependence with a small magnitude less than 2 mΩ cm at 800 K, indicating that the metallic conduction is robust against impurities. The robust metallic conduction further suggests that this class of oxide is a promising candidate for electrical leads at high temperature, which might replace platinum. A detailed measurement and analysis on the Hall resistivity have revealed that at least two components are responsible for the electrical conduction, in which a large number of electrons of moderate mobility coexist with a much smaller number of holes of extremely high mobility. This large electron density well screens the impurity potential and retains the metallic conduction against 7% impurity doping.
    AlkuperäiskieliEnglanti
    Artikkeli035104
    Sivut1-6
    JulkaisuJournal of Applied Physics
    Vuosikerta118
    Numero3
    DOI - pysyväislinkit
    TilaJulkaistu - 2015
    OKM-julkaisutyyppiA1 Julkaistu artikkeli, soviteltu

    Sormenjälki

    Sukella tutkimusaiheisiin 'An origin of good electrical conduction in La4BaCu5O13+δ'. Ne muodostavat yhdessä ainutlaatuisen sormenjäljen.

    Siteeraa tätä