An experimental study on the phase equilibria of FeOx-saturated iron silicate slags and metallic copper alloys at 1200–1300 °C

Min Chen, Katri Avarmaa, Pekka Taskinen, Radoslaw Michallik, Ari Jokilaakso*

*Tämän työn vastaava kirjoittaja

Tutkimustuotos: LehtiartikkeliArticleScientificvertaisarvioitu

13 Lataukset (Pure)

Abstrakti

The equilibrium phase relations between metallic copper alloys and magnetite/wüstite-saturated iron silicate slags were investigated at 1200–1300 °C and PO2 of 10−10 to 10−6.5 atm. The experiments involved high-temperature equilibration of samples in a controlled CO–CO2 atmosphere, followed by rapid drop quenching and direct measurement of the phase composition using the electron probe microanalysis technique. The equilibrium compositions for the metal and slag phase at different temperatures were displayed as a function of PO2. The present experimental results were compared with data from the literature as well as the thermodynamic assessment using MTDATA thermodynamic software. The present results contribute to the improvement of copper matte and black copper converting and slag cleaning processes.

AlkuperäiskieliEnglanti
Artikkeli102418
Sivumäärä12
JulkaisuCalphad: Computer Coupling of Phase Diagrams and Thermochemistry
Vuosikerta77
Varhainen verkossa julkaisun päivämäärä5 maalisk. 2022
DOI - pysyväislinkit
TilaJulkaistu - kesäk. 2022
OKM-julkaisutyyppiA1 Julkaistu artikkeli, soviteltu

Sormenjälki

Sukella tutkimusaiheisiin 'An experimental study on the phase equilibria of FeOx-saturated iron silicate slags and metallic copper alloys at 1200–1300 °C'. Ne muodostavat yhdessä ainutlaatuisen sormenjäljen.

Siteeraa tätä