Albumin Stabilized Fe@C Core–Shell Nanoparticles as Candidates for Magnetic Hyperthermia Therapy

Maria Antonieta Ramírez-Morales, Anastasia E. Goldt*, Polina M. Kalachikova, Javier A. Ramirez B, Masashi Suzuki, Alexey N. Zhigach, Asma Ben Salah, Liliya I. Shurygina, Sergey D. Shandakov, Timofei Zatsepin, Dmitry V. Krasnikov, Toru Maekawa, Evgeny N. Nikolaev, Albert G. Nasibulin*

*Tämän työn vastaava kirjoittaja

Tutkimustuotos: LehtiartikkeliArticleScientificvertaisarvioitu

1 Sitaatiot (Scopus)
91 Lataukset (Pure)

Abstrakti

Carbon-encapsulated iron nanoparticles (Fe@C) with a mean diameter of 15 nm have been synthesized using evaporation–condensation flow–levitation method by the direct iron-carbon gas-phase reaction at high temperatures. Further, Fe@C were stabilized with bovine serum albumin (BSA) coating, and their electromagnetic properties were evaluated to test their performance in magnetic hyperthermia therapy (MHT) through a specific absorption rate (SAR). Heat generation was observed at different Fe@C concentrations (1, 2.5, and 5 mg/mL) when applied 331 kHz and 60 kA/m of an alternating magnetic field, resulting in SAR values of 437.64, 129.36, and 50.4 W/g for each concentration, respectively. Having such high SAR values at low concentrations, obtained material is ideal for use in MHT.

AlkuperäiskieliEnglanti
Artikkeli2869
Sivumäärä9
JulkaisuNanomaterials
Vuosikerta12
Numero16
DOI - pysyväislinkit
TilaJulkaistu - elok. 2022
OKM-julkaisutyyppiA1 Alkuperäisartikkeli tieteellisessä aikakauslehdessä

Sormenjälki

Sukella tutkimusaiheisiin 'Albumin Stabilized Fe@C Core–Shell Nanoparticles as Candidates for Magnetic Hyperthermia Therapy'. Ne muodostavat yhdessä ainutlaatuisen sormenjäljen.

Siteeraa tätä