Al2O3-cBN composites sintered by SPS and HPHT methods

Tutkimustuotos: Lehtiartikkeli

Tutkijat

Organisaatiot

  • Institute of Advanced Manufacturing Technology
  • Institut de Physique des Materiaux, Bucarest-Magurele

Kuvaus

Spark Plasma Sintering (SPS) and High Pressure-High Temperature (HPHT) methods were chosen in order to study the behaviour of metastable cubic boron nitride (cBN) during sintering of Al2O3 +30vol.% cBN composites at low and high pressure. Relatively low sintering temperatures were used to avoid the undesired reverse transformation of cBN to hexagonal, graphite-like form. The microstructure, and phase composition as well as physical and mechanical properties of the resulting Al2O3-cBN composites were investigated. In the ball-on-disc tests, the coefficient of friction and the specific wear rate of the sintered samples were determined by rotating the sample against a stationary alumina ball. The best composites obtained by SPS (at 1300°C/75MPa) had slightly lower density, Young's modulus and hardness than those obtained by HPHT but their wear resistance was much better. Formation of hBN was suppressed up to 1300°C during SPS consolidation at the pressure of 75MPa.

Yksityiskohdat

AlkuperäiskieliEnglanti
Sivut1783-1789
JulkaisuJournal of the European Ceramic Society
Vuosikerta36
Numero7
TilaJulkaistu - 2016
OKM-julkaisutyyppiA1 Julkaistu artikkeli, soviteltu

ID: 2445046