A two-anode reduction technique to monitor the defect and dope the surface of TiO2 nanotube array as photo-anode for water splitting

Xuelan Hou, Shaohong Jiang, Yongdan Li*

*Tämän työn vastaava kirjoittaja

Tutkimustuotos: LehtiartikkeliArticleScientificvertaisarvioitu

17 Sitaatiot (Scopus)
69 Lataukset (Pure)

Abstrakti

A two-anode reduction (TAR) technique is adopted to prepare, in one step without the existence of gaseous hydrogen, black TiO2 nanotubes co-doped with carbon and nitrogen. A sample prepared with the TAR technique for 2 min achieved the highest photocurrent response as 2.05 mA/cm2, which is 3 times as high as that of the pristine TiO2 nanotubes. A synergistic effect between black hydrogenation and C, N co-doping is observed. The light absorption in the whole ultraviolet-visible (UV–vis) range is also greatly enhanced.

AlkuperäiskieliEnglanti
Artikkeli117949
JulkaisuApplied Catalysis B: Environmental
Vuosikerta258
DOI - pysyväislinkit
TilaJulkaistu - 5 jouluk. 2019
OKM-julkaisutyyppiA1 Alkuperäisartikkeli tieteellisessä aikakauslehdessä

Sormenjälki

Sukella tutkimusaiheisiin 'A two-anode reduction technique to monitor the defect and dope the surface of TiO2 nanotube array as photo-anode for water splitting'. Ne muodostavat yhdessä ainutlaatuisen sormenjäljen.

Siteeraa tätä