A future application of pulse plating–silver recovery from hydrometallurgical bottom ash leachant

Tutkimustuotos: Lehtiartikkelivertaisarvioitu

Tutkijat

Organisaatiot

Kuvaus

In the current study, electrodeposition-redox replacement was applied to a hydrometallurgical solution with the main elements of Ca (13.8 g L−1), Al (4.7 g L−1), Cu (2.5 g L−1), Zn (1.2 g L−1), Fe (1.2 g L−1), S (1 g L−1), Mg (0.8 g L−1), P (0.5 g L−1) and Ag (3.5 ppm). The solution originated from the leaching experiment of incinerator plant bottom ash, which was dissolved into 2 M HCl media at T = 30 °C. The resulting deposit on the electrode surface was analysed with SEM-EDS and the observed Ag/(Cu + Zn) ratio (0.3) indicated remarkable enrichment of silver on the surface, when compared to the ratio of these elements (Ag/(Cu + Zn)) in the solution (6.8 × 10−5). The enrichment of Ag vs. (Cu + Zn) could be demonstrated to increase ca. 4500 fold compared to the ratio of the elements in solution.

Yksityiskohdat

AlkuperäiskieliEnglanti
Sivut253-257
Sivumäärä5
JulkaisuTransactions of the Institute of Metal Finishing
Vuosikerta96
Numero5
TilaJulkaistu - 3 syyskuuta 2018
OKM-julkaisutyyppiA1 Julkaistu artikkeli, soviteltu

Lataa tilasto

Ei tietoja saatavilla

ID: 28528955