Surface passivation of black silicon phosphorus emitters with atomic layer deposited SiO2/Al2O3 stacks

Research output: Chapter in Book/Report/Conference proceedingConference contributionScientificpeer-review

Researchers

Research units

  • Arizona State University

Abstract

Black silicon (b-Si) is a promising surface structure for solar cells due to its low reflectance and excellent light trapping properties. While atomic layer deposited (ALD) Al2O3 has been shown to passivate efficiently lightly-doped b-Si surfaces and boron emitters, the negative fixed charge characteristic of Al2O3 thin films makes it unfavorable for the passivation of more commonly used n+ emitters. This work studies the potential of ALD SiO2/Al2O3 stacks for the passivation of b-Si phosphorus emitters fabricated by an industrially viable POCl3 gas phase diffusion process. The stacks have positive charge density (Qtot = 5.5·1011 cm-2) combined with high quality interface (Dit = 2.0·1011 cm-2eV-1) which is favorable for such heavily-doped n-type surfaces. Indeed, a clear improvement in emitter saturation current density, J0e, is achieved with the stacks compared to bare Al2O3 in both b-Si and planar emitters. However, although the positive charge density in the case of black silicon is even higher (Qtot = 2.0·1012 cm-2), the measured J0e is limited by the recombination in the emitter due to heavy doping of the nanostructures. The results thus imply that in order to obtain lower saturation current density on b-Si, careful optimization of the black silicon emitter profile is needed.

Details

Original languageEnglish
Title of host publication7th International Conference on Silicon Photovoltaics, SiliconPV 2017
Publication statusPublished - 21 Sep 2017
MoE publication typeA4 Article in a conference publication
EventInternational Conference on Crystalline Silicon Photovoltaics - Freiburg, Germany, Freiburg, Germany
Duration: 3 Apr 20175 Apr 2017
Conference number: 7
http://siliconpv.com/home.html

Publication series

NameEnergy Procedia
PublisherElsevier
Volume124
ISSN (Electronic)1876-6102

Conference

ConferenceInternational Conference on Crystalline Silicon Photovoltaics
Abbreviated titleSiliconPV 2017
CountryGermany
CityFreiburg
Period03/04/201705/04/2017
Internet address

    Research areas

  • black silicon, surface passivation, phosphorus diffusion, atomic layer deposition, SiO2, Al2O3

Download statistics

No data available

ID: 15342105