Rapid thermal anneal activates light induced degradation due to copper redistribution

Research output: Contribution to journalArticleScientificpeer-review

Researchers

Research units

  • University of New South Wales

Abstract

While it is well known that copper impurities can be relatively easily gettered from the silicon bulk to the phosphorus or boron-doped surface layers, it has remained unclear how thermally stable the gettering actually is. In this work, we show experimentally that a typical rapid thermal anneal (RTA, a few seconds at 800 °C) used commonly in the semiconductor and photovoltaic industries is sufficient to release a significant amount of Cu species from the phosphorus-doped layer to the wafer bulk. This is enough to activate the so-called copper-related light-induced degradation (Cu-LID) which results in significant minority carrier lifetime degradation. We also show that the occurrence of Cu-LID in the wafer bulk can be eliminated both by reducing the RTA peak temperature from 800 °C to 550 °C and by slowing the following cooling rate from 40-60 °C/s to 4 °C/min. The behavior is similar to what is reported for Light and Elevated Temperature degradation, indicating that the role of Cu cannot be ignored when studying other LID phenomena. Numeric simulations describing the phosphorus diffusion and the gettering process reproduce the experimental trends and elucidate the underlying physical mechanisms.

Details

Original languageEnglish
Article number032104
JournalApplied Physics Letters
Volume113
Issue number3
Publication statusPublished - 16 Jul 2018
MoE publication typeA1 Journal article-refereed

Download statistics

No data available

ID: 26865403