Determination of metallization degree of pre-reduced chromite with image and Rietveld analysis

T. Leino, P. Taskinen*, R. H. Eric

*Corresponding author for this work

Research output: Contribution to journalArticleScientificpeer-review

11 Downloads (Pure)

Abstract

Metallization degree of pre-reduced chromite was determined using two methods. The chromite samples were reduced in the solid state by methane-hydrogen gas mixtures. First method was image analysis of micrographs obtained by scanning electron microscope where heavier metallic phases appeared as bright white areas which were relatively easy to segment using a thresholding algorithm. The second technique was Rietveld analysis of X-ray powder diffraction pattern which fitted a calculated profile onto a measured X-ray diffraction pattern to gain information about phase quantities. Rietveld refinement and phase composition analysis was performed with PANalytical's X'Pert HighScore Plus software from the XRPD (X-ray powder diffraction) data. Both techniques were in good agreement. Metallization degrees for the investigated samples ranged from 15 to 65 % depending on the extent of reduction which was a function of time, reduction temperature, and methane content of the gas mixture. These results were promising and indicate that either image analysis or X-ray Rietveld analysis can be used as a relatively fast method to determine the degree of metallization of pre-reduced samples in comparison to the slow and tedious chemical analysis.

Original languageEnglish
Pages (from-to)289-297
Number of pages9
JournalJournal of Mining and Metallurgy, Section B: Metallurgy
Volume56
Issue number3
DOIs
Publication statusPublished - 2020
MoE publication typeA1 Journal article-refereed

Keywords

  • Analiza slike
  • Ferrous chromite
  • Gvožde hromit
  • Image analysis
  • Metalizacija
  • Metallization
  • Rietveld analysis
  • Rietveldova analiza

Fingerprint

Dive into the research topics of 'Determination of metallization degree of pre-reduced chromite with image and Rietveld analysis'. Together they form a unique fingerprint.

Cite this