Influence of surface roughness on high temperature fatigue strength and cracks initiation in 40CrMoV13.9 notched components

P. Gallo*, F. Berto

*Corresponding author for this work

Research output: Contribution to journalArticleScientificpeer-review

25 Citations (Scopus)

Abstract

The present paper addresses experimentally the high temperature fatigue of 40CrMoV13.9 steel and the effect of surface roughness on fatigue strength and cracks initiation.The 40CrMoV13.9 steel considered here is widely used in different engineering high temperature applications among which hot-rolling of metals, where, in order to assure a constant temperature, the rolls are provided with cooling channels. These are the most stressed zone of the rolls where cracks initiate systematically.In order to completely characterize the high temperature behaviour of this steel, firstly uniaxial-tension load controlled fatigue tests have been conducted at different temperatures up to 650. °C. Two geometries are considered: plain specimens and plates weakened by symmetric V-notches, with opening angle and tip radius being equal to 90° and 1. mm, respectively. Subsequently, with the aim to investigate the influence of the cooling channels roughness on the high temperature behaviour and the cracks initiation, uniaxial-tension load controlled fatigue tests have been conducted on plate with central hole at the service temperature of 650. °C, varying the surface roughness.After a brief review of the recent literature, the experimental procedure is described in detail and the new data from un-notched and notched specimens are summarized in terms of stress range, at the considered temperatures.Finally, fatigue data from un-notched and notched specimens are re-analyzed by means of the mean value of the Strain Energy Density (SED) extended at high temperature.

Original languageEnglish
Pages (from-to)226-234
Number of pages9
JournalTheoretical and Applied Fracture Mechanics
Volume80
DOIs
Publication statusPublished - 1 Dec 2015
MoE publication typeA1 Journal article-refereed

Keywords

  • 40CrMoV13.9
  • Cracks growth
  • High temperature fatigue
  • Strain energy density
  • Surface roughness

Fingerprint Dive into the research topics of 'Influence of surface roughness on high temperature fatigue strength and cracks initiation in 40CrMoV13.9 notched components'. Together they form a unique fingerprint.