@techreport{55e6e22181f04dc29cfe4712bec4ff81,
title = "Hot Cracking and Environment-assisted Cracking Susceptibility of Dissimilar Metal Welds",
keywords = "austenitic stainless steels, carbon steels, crack initiation, crack growth, dissimilar metal welds, environment-assisted cracking, hot cracking, microstructural analysis, nickel base alloys, nuclear power plants, residual stress measurement, Varestraint tests, weldability, austenitic stainless steels, carbon steels, crack initiation, crack growth, dissimilar metal welds, environment-assisted cracking, hot cracking, microstructural analysis, nickel base alloys, nuclear power plants, residual stress measurement, Varestraint tests, weldability, austenitic stainless steels, carbon steels, crack initiation, crack growth, dissimilar metal welds, environment-assisted cracking, hot cracking, microstructural analysis, nickel base alloys, nuclear power plants, residual stress measurement, Varestraint tests, weldability",
author = "Hannu H{\"a}nninen and Anssi Brederholm and Tapio Saukkonen and Hans Gripenberg and Aki Toivonen and Ulla Ehrnsten and Pertti Aaltonen",
year = "2007",
language = "English",
isbn = "978-951-38-6952-6",
series = "VTT Tiedotteita - Research Notes",
publisher = "Valtion teknillinen tutkimuskeskus",
number = "2399",
pages = "182",
type = "WorkingPaper",
institution = "Valtion teknillinen tutkimuskeskus",
}