Factors Affecting Low Temperature Crack Propagation (LTCP) Susceptibility of Nickel-Based Alloy 182, 82, 152 and 52 Weld Metals

Matias Ahonen; Ulla Ehrnstén; Tapio Saukkonen; Olga Todoshchenko; Hannu Hänninen

Factors Affecting Low Temperature Crack Propagation (LTCP) Susceptibility of Nickel-Based Alloy 182, 82, 152 and 52 Weld Metals

Matias Ahonen, Ulla Ehrnstén, Tapio Saukkonen, Olga Todoshchenko, Hannu Hänninen

Research output: Chapter in Book/Report/Conference proceeding › Conference article in proceedings › Scientific › peer-review

Original language	English
Title of host publication	17th International Conference on Environmental Degradation of Materials in Nuclear Power Systems Water Reactors August 9-13, 2015, Ottawa, Ontario, Canada
Pages	18
ISBN (Electronic)	978-1-926773-19-3
Publication status	Published - 2015
MoE publication type	A4 Conference publication

Keywords

fracture resistance
hydrogen trapping
low temperature crack propagation
nickel-based weld metal alloys

Cite this

Ahonen, M., Ehrnstén, U., Saukkonen, T., Todoshchenko, O., & Hänninen, H. (2015). Factors Affecting Low Temperature Crack Propagation (LTCP) Susceptibility of Nickel-Based Alloy 182, 82, 152 and 52 Weld Metals. In 17th International Conference on Environmental Degradation of Materials in Nuclear Power Systems Water Reactors August 9-13, 2015, Ottawa, Ontario, Canada (pp. 18)

@inproceedings{821e22540b944926b82a191a275190e5,

title = "Factors Affecting Low Temperature Crack Propagation (LTCP) Susceptibility of Nickel-Based Alloy 182, 82, 152 and 52 Weld Metals",

keywords = "fracture resistance, hydrogen trapping, low temperature crack propagation, nickel-based weld metal alloys, fracture resistance, hydrogen trapping, low temperature crack propagation, nickel-based weld metal alloys, fracture resistance, hydrogen trapping, low temperature crack propagation, nickel-based weld metal alloys",

author = "Matias Ahonen and Ulla Ehrnst{\'e}n and Tapio Saukkonen and Olga Todoshchenko and Hannu H{\"a}nninen",

note = "VK: T20309",

year = "2015",

language = "English",

pages = "18",

booktitle = "17th International Conference on Environmental Degradation of Materials in Nuclear Power Systems Water Reactors August 9-13, 2015, Ottawa, Ontario, Canada",

}

Ahonen, M, Ehrnstén, U, Saukkonen, T, Todoshchenko, O & Hänninen, H 2015, Factors Affecting Low Temperature Crack Propagation (LTCP) Susceptibility of Nickel-Based Alloy 182, 82, 152 and 52 Weld Metals. in 17th International Conference on Environmental Degradation of Materials in Nuclear Power Systems Water Reactors August 9-13, 2015, Ottawa, Ontario, Canada. pp. 18.

Factors Affecting Low Temperature Crack Propagation (LTCP) Susceptibility of Nickel-Based Alloy 182, 82, 152 and 52 Weld Metals. / Ahonen, Matias; Ehrnstén, Ulla; Saukkonen, Tapio et al.
17th International Conference on Environmental Degradation of Materials in Nuclear Power Systems Water Reactors August 9-13, 2015, Ottawa, Ontario, Canada. 2015. p. 18.

Research output: Chapter in Book/Report/Conference proceeding › Conference article in proceedings › Scientific › peer-review

TY - GEN

T1 - Factors Affecting Low Temperature Crack Propagation (LTCP) Susceptibility of Nickel-Based Alloy 182, 82, 152 and 52 Weld Metals

AU - Ahonen, Matias

AU - Ehrnstén, Ulla

AU - Saukkonen, Tapio

AU - Todoshchenko, Olga

AU - Hänninen, Hannu

N1 - VK: T20309

PY - 2015

Y1 - 2015

KW - fracture resistance

KW - hydrogen trapping

KW - low temperature crack propagation

KW - nickel-based weld metal alloys

KW - fracture resistance

KW - hydrogen trapping

KW - low temperature crack propagation

KW - nickel-based weld metal alloys

KW - fracture resistance

KW - hydrogen trapping

KW - low temperature crack propagation

KW - nickel-based weld metal alloys

M3 - Conference article in proceedings

SP - 18

BT - 17th International Conference on Environmental Degradation of Materials in Nuclear Power Systems Water Reactors August 9-13, 2015, Ottawa, Ontario, Canada

ER -