Experimental evaluation of rolling contact fatigue in railroad wheels

Research output: Contribution to journalArticleScientificpeer-review

Details

Original languageEnglish
Pages (from-to)158-170
Number of pages13
JournalINTERNATIONAL JOURNAL OF FATIGUE
Volume91
Publication statusPublished - 1 Oct 2016
MoE publication typeA1 Journal article-refereed

Researchers

Research units

  • Illinois Institute of Technology
  • Norwegian University of Science and Technology
  • Polytechnic University of Bari
  • University of Padova

Abstract

Surface damage in railroad wheels is a very complex phenomenon and the contact fatigue plays a fundamental role in the damage process. In the case of railroad wheels the actual fracture process is quite different from the conventional idea of fracture in a load bearing structural component. The cracks that are generated by contact fatigue are not the source of actual wheels cracking but lead to the damaging phenomenon called shelling which implies separation of chunks of material from the surface. Shelling is mainly due to the presence of a fluid in the contact area, which penetrates in the fatigue cracks and causes a crack propagation leading to the separation of a portion of the wheel surface. A basic starting point to analyze this phenomenon is to study the crack development in the contact surface and to evaluate the behavior of different types of steels used for wheels manufacturing. However, the challenge to obtain a reliable similitude between laboratory and real conditions is far from straightforward. The present paper illustrates an experimental approach for rolling contact fatigue and shelling evaluation based on the possibility of simulating, in the laboratory, boundary conditions that can be scaled to the actual railroad, thus providing a realistic evaluation of the contact fatigue life of different steels.

    Research areas

  • Crack propagation, Fatigue, Rail vehicles, Railway engineering, Rolling contact fatigue