Effects of Static Strain Aging on Mechanical Performance of Ductile Cast Iron

EN-GJS-400-15U nodular cast iron intended to be used as load-bearing element in long-term geological disposal canisters containing spent nuclear fuel in Finland and Sweden was studied for static strain aging (SSA). Tensile test specimens manufactured from the nodular cast iron were pre-strained to 1%, 2% and 3% nominal plastic strains. The pre-strained specimens were aged at different temperatures ranging from room temperature to 400 °C for varying times. The aged specimens were tested with conventional tensile testing using constant cross-head speed of 0.016 mm/s. Additionally, four specimens were studied with digital image correlation (DIC) during the tensile testing to obtain full-field strain measurements. SSA resulted in elevated pronounced yield point in all the conditions, while the as-received material showed continuous yielding behavior. SSA reduced the elongation to fracture. DIC tests showed more localized yielding behavior in the SSA specimens. Over-aging effect was observed at 400 °C where increasing pre-strain did not increase the yield stress more. For 1-day aging time, the highest yield stress increment was found after aging at 200°C. The yield stress of the material was almost identical after aging in 100°C and 200°C.