Effect of Hot Cracks on EAC Crack Initiation and Growth in Nickel-base Alloy Weld Metals

Hannu Hänninen, Aki Toivonen, Anssi Brederholm, Tapio Saukkonen, Wade Karlsen, Ulla Ehrnsten, Pertti Aaltonen

Research output: Chapter in Book/Report/Conference proceedingConference contributionScientificpeer-review

2 Citations (Scopus)
Original languageEnglish
Title of host publication15th International Conference on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors
EditorsJeremy T. Busby, Gabriel Ilevbare, Peter L. Andresen
Place of PublicationUSA
Pages197-222
Number of pages26
ISBN (Electronic)9781118456835
Publication statusPublished - 2012
MoE publication typeA4 Article in a conference publication
EventInternational Conference on Environmental Degradation of Materials in Nuclear Power Systems and Water Reactors - Colorado Springs, United States
Duration: 7 Aug 201111 Aug 2011
Conference number: 15

Conference

ConferenceInternational Conference on Environmental Degradation of Materials in Nuclear Power Systems and Water Reactors
Abbreviated titleED
CountryUnited States
CityColorado Springs
Period07/08/201111/08/2011

Keywords

  • electron microscopy
  • environment-assisted cracking
  • hot cracking
  • Laves phase
  • nickel-base alloys
  • weld metal

Cite this

Hänninen, H., Toivonen, A., Brederholm, A., Saukkonen, T., Karlsen, W., Ehrnsten, U., & Aaltonen, P. (2012). Effect of Hot Cracks on EAC Crack Initiation and Growth in Nickel-base Alloy Weld Metals. In J. T. Busby, G. Ilevbare, & P. L. Andresen (Eds.), 15th International Conference on Environmental Degradation of Materials in Nuclear Power Systems-Water Reactors (pp. 197-222).