Corrigendum to: Hydrogen effects on mechanical performance of nodular cast iron (Corrosion Reviews 37:5 (441–454) DOI: 10.1515/corrrev-2019-0007)

Antti Forsström*, Yuriy Yagodzinskyy, Hannu Hänninen

*Corresponding author for this work

Research output: Other contributionScientificpeer-review

Abstract

The corrigendum corrects some of the figures include in the original article. The following points need to be corrected: - The nominal strains in Figure 7b should be an order of magnitude lower. (Figure Presented) Therefore, the creep rates in Figure 8 should also be an order of magnitude lower. - The naming of two specimens in Figure 8 is incorrect. CIK_B_CLT_Water_02 should be CIK_A_CLT_Water_02, and CIK_A_CLT_Air_01 should be CIK_B_CLT_Air_01. - The CLT of both studied types of cast iron under continuous hydrogen charging results in an increased strain rate of up to 2 × 10-7 s-1 when compared to CLT in air and distilled water, where the strain rate was about 2 × 10-9 s-1. – The corrected figures are shown below. The authors apologize for any inconvenience caused. (Figure Presented).

Original languageEnglish
DOIs
Publication statusPublished - 28 Dec 2019
MoE publication typeNot Eligible

Publication series

NameCorrosion Reviews
PublisherFreund Publishing House Ltd
ISSN (Print)0334-6005

Fingerprint Dive into the research topics of 'Corrigendum to: Hydrogen effects on mechanical performance of nodular cast iron (Corrosion Reviews 37:5 (441–454) DOI: 10.1515/corrrev-2019-0007)'. Together they form a unique fingerprint.

Cite this